MICROGRAPH

PHYSICAL DATA
Cold crushing strength1 | >200 N/mm2 |
Refractoriness under load (T05)2 | 1700°C |
Corrosion resistance in soda lime glass at 1550°C3 | index 0.71 (referred to 1240 material) |
Stone formation in soda lime glass at 1500°C | 0 |
Blistering in soda lime glass at 1150°C4-5 | 0 |
Exudation at 1550°C6 | index 1 (reference index) |
True density7 | 3.79 g/cm3 |
1 DIN EN 993-5
2 DIN EN ISO 1893
3 ICG TC11, 120 hours
4 Crucible test, 96 hours
5 ICG Subcommittee A1 definition
6 ICG TC11, 10 cycles
7 DIN 66137-2
TYPICAL CHEMICAL COMPOSITION
TYPICAL MINERALOGICAL COMPOSITION
THERMAL CONDUCTIVITY
ELECTRICAL RESISTIVITY
THERMAL EXPANSION
CASTING TYPE

- Contact us for
- Technical data sheet
- Contact us for
- Catalog
- For sizes please contact
- REFEL Engineering Service